タイトル：ソーダ沸石の圧力誘起アモルファス化への圧力媒体の影響
Title : Hydrostatic effect on the pressure-induced amorphization of natrolite
要旨：
Zeolites are hydrous aluminosilicates with a microporous structure, which can incorporate water and various gas molecules due to their characteristic microporous framework structure. Naturally occurring in the surface layers of the Earth and Mars, synthesized zeolites also have very important industrial applications as ion exchange materials, catalysts and adsorbents depending on the size of the pores.
Natrolite has the chemical formula Na2(Si3Al2)O10·2H2O and has four- and eight-membered ring (MR) structures in its crystal structure composed of SiO6 and AlO6 linkages. Sodium ions and H2O molecules are arranged in the 8MR and other cations can be exchanged for the Na+ cation part. In previous studies, natrolite is known to incorporate more water while undergoing reversible pressure-induced phase transitions up to 1.5 GPa (Liu et al. 2010; 2013). At 7−10 GPa, amorphization occurs in water or 4 : 1 methanol-ethanol mixture (ME) as a “penetrating” pressure-transmitting medium (PTM) (Goryainov et al. 2005; 2013). However, there are discrepancies in their reported amorphization pressures. In this study, therefore, the influence of the PTM on amorphization of natural natrolite has been examined. The ultimate goal is to clarify its possibility of water reservoir and reaction with atmospheric nitrogen in the Martian environments.
High-pressure experiments were carried out in a diamond anvil cell (DAC) using water, ME or nitrogen as a PTM. In situ observations at room temperature and high pressure via Raman spectroscopy and synchrotron X-ray diffraction were performed. Based on the present results, natrolite was stable under much higher pressure (>10 GPa) than previously reported. Amorphization pressures had no correlation with the molecular size. The alcohol mixture (ME) expands the cell volume, suggesting the methanol/ethanol insertion into 8MR. Nitrogen showed a unique splitting for both Raman bands and Bragg reflections. It is indicated that nitrogen is incorporated into 4MR causing the structural distortion and accelerating the amorphization. The interaction of natrolite with nitrogen in the Martian surface may affect the ability of natrolite to retain water in the subsurface and much deeper environment.
発表者： 鈴木 敏弘
Speaker : Suzuki Toshihiro
タイトル：3次元データの2次元画面への表示方法
Title : How to display 3D data on a 2D display
要旨：
３次元的な測定によるデータ収集は、レーザーアブレーションを用いた質量分析測定に限らず、医療分野でのX線CT検査やMRI検査など、現在では幅広く用いられるようになった。得られた３次元データは、パソコンなどを用いて処理されるので、測定結果を２次元画面上に表示する必要がある。
3次元データ解析で一般的に用いられている方法としては、測定結果に対して閾値を設定して「境界面」を求め、その境界面を3次元空間に存在する表面として表現する方法がある。この方法を用いれば、3次元空間の境界面を２次元平面に投影する事により、対象物の形状をモニター画面に表示する事が出来る。しかし、この方法は表面を表示するだけであり、物体内部の組成分布状態などを観察する事は難しい。
現在作成しているプログラムでは、各測定点を３次元空間に存在する長方形として表示させているが、測定値に応じで色と透明度を変化させている。この方法では、測定値が大きな領域は不透明で比較的明瞭に見えるが、測定値が低い領域は、ほぼ透明になる。この方法を用いて対象範囲を回転させながら透明度を変化させる、等の操作により物体内部の組成変化等も２次元画面上から観察する事がある程度は可能である。